Adrien

Custer feldspar                  52.1
Whiting                            8.9
Zinc oxide                        8
Barium carbonate             21
Ball clay                         10

Total                            100

Rutile                            2 

Copper carbonate           0.3

Red iron oxide               2.5

Na2O  0.06    Al2O3  0.30      SiO2  1.81

K2O  0.15                            TiO2  0.07

MgO  0.00                            Fe2O3  0.05

CaO  0.24                              

CuO  0.01                              

ZnO  0.26                              

BaO  0.28                              

Alumina:Silica ratio is  1.00:6.00

Neutral:Acid ratio is    1.00:6.37

Alk:Neut:Acid ratio is 1.00:0.30:1.92

Expansion: 93.7 x 10e-7 per degree C

--------------------------------------------

B.G. Green

Nepheline syenite           45
Talc                              7
Dolomite                     10
Whiting                        8
Silica                          29

Total                         100

Bentonite                     3

Red iron oxide             2

Manganese dioxide       1

Na2O  0.21    Al2O3  0.30     SiO2  2.77

K2O  0.06                            TiO2  0.00

MgO  0.29                           Fe2O3  0.04

CaO  0.40                              

MnO  0.03                              

Alumina:Silica ratio is  1.00:9.39

Neutral:Acid ratio is    1.00:9.51

Alk:Neut:Acid ratio is 1.00:0.30:2.81

Expansion: 75.1 x 10e-7 per degree C

---------------------------------------------

M.S, Orange Brown

Dolomite                18
Whiting                  3
Custer feldspar       54
EPK                     25

Total                   100

Zircopax              5

Red iron oxide      1.5

Na2O  0.08    Al2O3  0.59      SiO2  2.67

K2O  0.19                             P2O5  0.00

MgO  0.31                           TiO2  0.00

CaO  0.42                            Fe2O3  0.04

                                          ZrO2  0.09

Alumina:Silica ratio is  1.00:4.55

Neutral:Acid ratio is    1.00:4.77

Alk:Neut:Acid ratio is 1.00:0.59:2.79

Expansion: 77.5 x 10e-7 per degree C

------------------------------------------

John Fell Blue

Nepheline syenite        70

Whiting                      5

Gerstley borate           2

Spodumene               15

EPK                          8

Total                       100

Black cobalt oxide     1

Rutile                       1

Na2O  0.45    Al2O3  0.86      SiO2  3.42

K2O  0.13     B2O3  0.03       P2O5  0.00

MgO  0.01                           TiO2  0.05

CaO  0.23                            Fe2O3  0.00

Li2O  0.13                              

CoO  0.05                              

Alumina:Silica ratio is  1.00:3.97

Neutral:Acid ratio is    1.00:3.88

Alk:Neut:Acid ratio is 1.00:0.89:3.47

Expansion: 86.1 x 10e-7 per degree C

Oxides causing abnormal expansion:

  Li2O  B2O3

-----------------------------------------

Julien Glossy White

Custer feldspar            62.5

Ball clay                      5.68

Spodumene                 9.09

Whiting                    17.05

Zinc oxide                 5.68

Total                        100

Zircopax                  12

Na2O  0.08    Al2O3  0.40      SiO2  2.56

K2O  0.19                            TiO2  0.00

MgO  0.00                           Fe2O3  0.00

CaO  0.48                           ZrO2  0.18

Li2O  0.06                              

 ZnO  0.19                              

Alumina:Silica ratio is  1.00:6.34

Neutral:Acid ratio is    1.00:6.80

Alk:Neut:Acid ratio is 1.00:0.40:2.75

Expansion: 83.0 x 10e-7 per degree C

Oxides causing abnormal expansion:

  Li2O

----------------------------------------

Transparent

Custer feldspar          30
Whiting                    20
Ball clay                   20
Silica                      30

Total                     100

Na2O  0.06    Al2O3  0.41      SiO2  4.08

K2O  0.14                             TiO2  0.02

MgO  0.01                            Fe2O3  0.01

CaO  0.80                              

Alumina:Silica ratio is  1.00:9.85

Neutral:Acid ratio is    1.00:9.90

Alk:Neut:Acid ratio is 1.00:0.41:4.10

Expansion: 67.9 x 10e-7 per degree C

------------------------------------------

Green Celadon

Custer feldspar       30    
Whiting                 20
Ball clay                20
Silica                    30

Total                   100

Red iron oxide      2

Na2O  0.06    Al2O3  0.41     SiO2  4.08

K2O  0.14                            TiO2  0.02

MgO  0.01                           Fe2O3  0.06

CaO  0.80                              

Alumina:Silica ratio is  1.00:9.85

Neutral:Acid ratio is    1.00:10.02

Alk:Neut:Acid ratio is 1.00:0.41:4.15

Expansion: 69.3 x 10e-7 per degree C

------------------------------------------

Turquoise

Custer feldspar                         41
Talc                                        13
Dolomite                                  9
Ball clay                                   5
3211                                       11
Silica                                      21
Total                                     100

Green chromium oxide               1
Cobalt carbonate                        1

Na2O  0.05    Al2O3  0.22       SiO2  2.64
K2O  0.12     B2O3  0.25       TiO2  0.00
MgO  0.39                           Cr2O3  0.02
CaO  0.41                            Fe2O3  0.00
MnO  0.00                            
CoO  0.02                            

Alumina:Silica ratio is  1.00:11.80
Neutral:Acid ratio is    1.00:5.68
Alk:Neut:Acid ratio is 1.00:0.47:2.67

Expansion: 66.9 x 10e-7 per degree C
Oxides causing abnormal expansion:
  B2O3

------------------------------------------

Black

Albany slip             100
Cobalt oxide              3

Na2O  0.05    Al2O3  0.56     SiO2  3.77
K2O  0.13                            TiO2  0.02
MgO  0.26                           Fe2O3  0.13
CaO  0.41                            
CoO  0.15                            

Alumina:Silica ratio is  1.00:6.71
Neutral:Acid ratio is    1.00:6.97
Alk:Neut:Acid ratio is 1.00:0.56:3.92

Expansion: 68.6 x 10e-7 per degree C

--------------------------------------------

Jeff Brown

Custer feldspar       48
Dolomite               10
Whiting                  2
Ball clay                 3
Silica                   30
Gerstley borate      5
Zinc oxide            2

Total                 100

Rutile                 4
Red iron oxide    6

Na2O  0.10    Al2O3  0.35      SiO2  4.20
K2O  0.20     B2O3  0.08       TiO2  0.19
MgO  0.23                            Fe2O3  0.15
CaO  0.37                            
ZnO  0.09                            

Alumina:Silica ratio is  1.00:12.05
Neutral:Acid ratio is    1.00:10.57
Alk:Neut:Acid ratio is 1.00:0.43:4.53

Expansion: 74.5 x 10e-7 per degree C
Oxides causing abnormal expansion:
  B2O3

---------------------------------------

G2A1

G-200 feldspar              41.1
Barium carbonate          16.6
Ball clay                       15.6
Whiting                        14.4
Zinc oxide                     6.3
Gerstley borate              3.9
Total                            97

Rutile                       1.5
Red iron oxide          1.5

Na2O  0.06    Al2O3  0.29     SiO2  1.51

K2O  0.12     B2O3  0.04      TiO2  0.05

MgO  0.01                          Fe2O3  0.03

CaO  0.41                              

ZnO  0.19                              

BaO  0.21                              

Alumina:Silica ratio is  1.00:5.20

Neutral:Acid ratio is    1.00:4.80

Alk:Neut:Acid ratio is 1.00:0.33:1.59

Expansion: 94.1 x 10e-7 per degree C

Oxides causing abnormal expansion:

  B2O3

-------------------------------------